Poly Butylene Terephthalate (PBT) 30% Glass Fiber PBT Stiffness and Dimensional Stability
Model NO.
PBT-WF006
EINECS
618-371-8
Material
Polybutylene Terephthalate/PBT
Usage
General Plastics, Engineering Plastics, Specialty Plastics
Plastic Properties After Heated
Thermoplastic Plastics
Plastic Forming Method
Injection
Color
Natural Color
Delivery Time
in 7 Days
Form
Resin Pellets
Glass Fiber
15%
Applications
Appliance Handles, Spotlights, Electric Motors.
Features
Lubricated, Good Wear Resistance, Low Friction and
Application
Zippers Irish Flutes, Bagpipes, Practice Chanters
Use
Radiator Front Cover.Automotive Parts
Place of Origin
Guangdong, China
Transport Package
Bag
Specification
25KG
Trademark
Forever
Origin
China
HS Code
390740000
Production Capacity
50000t/Year
Package Size
75.00cm * 55.00cm * 15.00cm
Package Gross Weight
25.010kg
Reference Price
$ 0.44 - 2.41
Description
Product Description
Poly butylene terephthalate (PBT) 30% glass fiber PBT Stiffness and Dimensional Stability
Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.
Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.
With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry
| Product Description | ||
|
LNP
ELCRIN WF006XiQ compound
is
based on
Poly
butylene terephthalate
(PBT)
resin
utilizin
g
ELCRIN
iQ
upcycling technology containing minimum 37% Post-Consumer Recycling (PCR) weight cont ent and 30% glass fiber. Added features of this grade include: Excellent Strength, Stiffness and Dimensional Sta bility. Potential applications may include ha ndles, connectors. |
||
| General | ||
| Form Resin Pellets | ||
| Filler 30 % Glass Fiber | ||
| Feature |
Good
Dimensional
Pcr |
Good Hardness 37 % Pcr |
| Uses |
Automotive
Electrical |
Connector Consumer |
| Physical Nominal Value Test Method | ||
|
Density / Specific
Gravity
1.54 ASTM D792 1.54 g/cm³ ISO 1183 |
||
| Water Absorption | ||
| 24 hrs;23 °C 0.1 % ASTM D570 | ||
| 23 °C;saturated 0.09 % ISO 62-1 | ||
| Mold Shrinkage, Flow(3.2 mm) 0.5 - 0.7 % SABIC Method | ||
| Mold Shrinkage, XFlow(3.2 mm) 0.8 - 1 % SABIC Method | ||
| Melt Flow Rate[MFR](250 °C;5 kgf) 52 g/10min ASTM D1238 | ||
| Moisture Absorption(50% RH;23 °C) 0.1 % ISO 62 | ||
| Melt Volume Rate, MVR(5 kg;MVR at 250 °C) 38 cm³/10 mi n ISO 1133 | ||
| Mechanical | Nominal Value | Test Method |
| Izod Impact, Unnotched(23 °C) | 770 J/m | ASTM D4812 |
| Izod Impact, Notched | ||
| 23 °C | 82 J/m | ASTM D256 |
| -30 °C | 83 J/m | ASTM D256 |
| 80*10*4;23 °C | 8 kJ/m² | ISO 180/1A |
| 80*10*4;-30 °C | 8 kJ/m² | ISO 180/1A |
| Instrumented Dart Impact, Total Energy(23 °C) | 7 J | ASTM D3763 |
| C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp = 62 mm 0) | 14 kJ/m² | ISO 179 1eA |
| Tensile Stress , Yield | ||
| 5 mm/min;Type I | 114 MPa | ASTM D638 |
| 5 mm/min | 139 MPa | ISO 527 |
| Tensile Stress, Break | ||
| 5 mm/min;Type I | 114 MPa | ASTM D638 |
| 5 mm/min | 139 MPa | ISO 527 |
| Tensile Strain , Yield | ||
| 5 mm/min;Type I | 2.2 % | ASTM D638 |
| 5 mm/min | 1.6 % | ISO 527 |
| Tensile Strain, Break | ||
| 5 mm/min;Type I | 2.2 % | ASTM D638 |
| 5 mm/min | 1.6 % | ISO 527 |
| Tensile Modulus | ||
| 5 mm/min | 1.2E+04 MPa | ASTM D638 |
| 1 mm/min | 1.1E+04 MPa | ISO 527 |
| Flexural Stress, Yie ld | ||
| 1.3 mm/min;50 mm;span | 210 MPa | ASTM D790 |
| 2 mm/min | 210 MPa | ISO 178 |
| Flexural Stress, break(1.3 mm/min;50 mm;span) | 189 MPa | ASTM D790 |
| Flexural Modulus | ||
| 1.3 mm/min;50 mm;span | 9100 MPa | ASTM D790 |
| 2 mm/min | 9100 MPa | ISO 178 |
| Thermal | Nominal Value | Test Method |
|
Heat
Deflection Temperature[HD
T],
Unannealed
3.2 mm;1.82 MPa 1.82 MPa;6.4 mm |
203 °C 207 °C |
ASTM D648 |
| CTE, Flow | ||
| -40 - 40 °C | 2.5e-05 1/°C | ASTM E831 |
| -40 - 40 °C | 2.5e-05 1/°C | ISO 11359-2 |
| CTE, XFlow | ||
| -40 - 40 °C | 8.9e-05 1/°C | ASTM E831 |
| -40 - 40 °C | 8.9e-05 1/°C | ISO 11359-2 |
| Ball Pressure Test, Approximate Maximum | 200 °C | IEC 60695-10-2 |
| HDT/Bf(0.45) | 217 °C | ISO 75/Bf |
| Electrical | Nominal Value | Test Method |
| Volume Resistivity | > 1E+15 ohms ·cm | ASTM D257 |
| Dielectric Strength, in Air(3. 2 mm) | 23 kV/mm | ASTM D149 |
| Processing | Nominal Value | |
| Drying Temperature < Injection > | 120 °C | |
| Drying Time<Injection> | 3 - 4 hrs | |
| Drying Time , Cumulative < Injection > | 12 hrs | |
| Maximum Moisture Content<Inject ion> | 0.02 % | |
| Melt Temperature < Injection > | 250 - 265 °C | |
| Nozzle Temperature < Injection > | 245 - 265 °C | |
| Front, Zone 3 Temperature<Injection> | 250 - 265 °C | |
| Middle , Zone 2 Temperature < Injection > | 245 - 260 °C | |
| Rear, Zone 1 Temperature<Inject ion> | 240 - 255 °C | |
| Mold Temperature < Injection > | 65 - 90 °C | |
| Back Pressure<Injection> | 0.3 - 0.7 MPa | |
| Screw Speed <Injection> | 50 - 80 rpm | |
| Shot To Cylinder Size < Injection > | 40 - 80 % | |
| Vent Depth <Injection> | 0.025 - 0.038 mm |
Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.
Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.
With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry
Plastic Materials
-
4.5 Inch 480* 854 Mipi Interface IPS Custom TFT LCD Panel TFT Module
High Quality Chemicals Peptide CAS 820959 -17-9 Acetyl Tetrapeptide-5 Reduces Puffy Eyebags Acetyl Tetrapeptide-5 Best Price
Factory Price Hand Carved Religious Church Altar Natural White Marble Altar Table
Aztreonam Sterile API Pharmaceutical Grade
CAS: 78110-38-0 Aztreonam
AC-Tyr-Arg-Ser-Arg-Lys-Tyr-Thr-Ser-Trp-Tyr-Nh2; Acetyl Decapeptide-3; CAS No.: 935288 -50-9 High-Purity 98%; High-Quality Anti-Wrinkle Multi-Peptides
Mccloskey J50 Premium Casting Mn18cr2 Jaw Liner for Crushing Gabbro
CAS 820959 -17-9 Anti Eye-Bags and Hair Growth Series Acetyl Tetrapeptide-5 Anti-Wrinkle & Anti-Aging Series Cosmetic Peptide
96 Well Plate Square V-Shape Bottom 2.2ml Laboratory Disposable Deep Well Plates with PCR Sealing Film
Multi-Purpose Oil Fuel Gasoline Low Pressure Hydraulic Rubber Hose En 854 / SAE 100 R6 Hose
Peptide Manufacturers Pharmaceutical Octreotide Acetate Peptide Powder CAS 83150 -76-9 Octreotide Sandostatin Powder Pharmaceutical Octreotide
Mn- Yd001 CE&ISO USA Pump Hydraulic Hospital Medical Stretcher
Oil Filter Wrench - Claw Type 75-120mm
Made in China Luffing Jib Crane Luffing Jib Crane Hammerhead Tower Crane
9ml Poly Bag Shampoo / Hotel Sachet
Hcnc Hsr -Hc415 4 Axis Robot Arm Industrial Stamping Robot
DREAMKITCHEN.PT, 2023